Cafco SPRAYFILM® WB3

Cafco® SPRAYFILM WB3 is a water based intumescent coating consisting of polyvinyl acetate resins and fillers for the fire protection of structural steel. It is preferably spray applied with airless paint equipment for speed and quality of finish. Brush and roller application is also possible.

Cafco® SPRAYFILM WB3 can be sealed and protected with a decorative top coat. Cafco® SPRAYFILM WB3 is applied directly to the contour of primed steel to provide fire protection for up to 120 minutes. In a fire, a chemical reaction takes place causing the Cafco® SPRAYFILM WB3 to expand and form an insulating layer which slows the temperature of the steel rising to a critical level.

Cafco SPRAYFILM® WB3 - APAC Packaging
Cafco SPRAYFILM® WB3 - APAC Packaging

Further Information

Applications:

  • Fire protection of steel structures.

Benefits:

  • Single pack water-based intumescent paint
  • Structural Steel Protection of up to 120 minutes
  • Compatible with commonly used primers
  • Compatible with many topcoats to provide durability for various usage category, from internal to external application
  • Produce a thin and seamless finish
  • Can be applied using brush, roller and also airless spray
  • For both open and hollow sections
  • Application onto galvanised steel is possible
  • Quick application and easy cleanup
  • Fast drying time
Approx. Curing Time ( µm after 8 hours 20°C, 50% humidity): 7 d
Density (kg/m³ ± 0.05kg/l): 1.36 g/cm³
Approx. Drying Time (hour at 20°C and 50% RH for 1 mm WFT): 6 h
Application Temperature Min (°C): 5 °C
Application Temperature Max (°C): 38 °C
Solids Content (%): 71 %
Viscosity (Pa.s at 20°C): 42000 cps
Colour: White
Shelf Life (months): 10 months
Storage Conditions: Storage Temperature 10ºC : 38ºC. Must protect from freezing and excessive heat. Store in a dry environment.
Storage Temperature Min (°C): 5 °C
Storage Temperature Max (°C): 40 °C

Please note
All physical and mechanical values are averages based on standard production and tested according to internal procedures. The typical values are given for guidance. The figures can change dependent on the test methods used. If a particular value is of prime importance for a specification, please consult Promat Technical Department.

 

Downloads

Related downloads

60 Years of Expertise

Tested & Certified Solutions

Global Service Network